Quick Details
- Brand Name:Rensino
- Shape: Arc
- Magnetic Power: N35-N52
- Color: Ni, sliver
- Composite: NdFeB Magnet
- Application: Industrial Magnet
- Type: Permanent
Packaging & Delivery
| Packaging Details: | By air: Use Iron to sheld the magnetic power, By sea: standard sea package |
|---|---|
| Delivery Detail: | 15-20 days |
Specifications
1.Many Grade: N, M, H, SH, UH, EH
2.Many shapes: Block, Ring, Disc and so on
3.Coating: Ni or others
4. Materials: Neodymium-Iron-Boron;
5. Magnetic properties: High coercive force, the max operation temp is up to 200 degree centigrade or 380 curie temperature;
6. Grades: N35-N52; 35M-50M; 35H-48H; 35SH-45SH; 30UH-40UH; 30EH-38EH;
7. Shapes and sizes: Various kinds or according to customers' request;
8. Coatings: Ni, Zn, gold, copper, epoxy, chemical, parylene and so on;
9. Applications: Widely used in different applications, such as sensors, motors, rotors, wind turbines/wind generators, loudspeakers, magnetic hooks, magnetic holder, filters automobiles and so on.
10.Certification: ISO9001:2008.
11.Technology: Utilizes new Sintered NdFeB magnet techniques and equipment such as strip casting, HDDR technology
Production Description
Plating Characteristics
| Plating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
| NiCuNi (Nickel Copper Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver plating layers are 1-2 μm thick.
Test results shown to allow comparison between plating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
Test results shown to allow comparison between plating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.