Quick Details
- Brand Name:Rensino
- Type: Permanent
- Composite: Neodymium Magnet
- Shape: Block
- Application: Industrial Magnet
- Coating: Ni
- Normal tolerance: +/- 2%mm
- Magnet grade: Y30, Y30BH
- Max working temperature: 60C-200C
- Sample: available
- Customized Design: available
- Urgent order: available
- Magnet orientation: through thickness
- OEM：Available
- Magnet situation: magnetized
Packaging & Delivery
| Packaging Details: | 1.Standard Air Way package(filled with iron sheets and foams to shield magnetism) 2.Standard Sea Way package(packed in carton and then put on a pallet) 3.Customized package is available |
|---|---|
| Delivery Detail: | 25-45 days |
Specifications
ISO9001:2008 and TS16949
accept mix or small order
different payment terms
10 years' export experience
free sample available
Production Description
Plating Characteristics
| Plating Type | Overall Thickness | Salt Spray Test | Pressure Cooker Test |
| NiCuNi (Nickel Copper Nickel) | 15-21 μm | 24 hours | 48 hours |
| NiCu + Black Nickel | 15-21 μm | 24 hours | 48 hours |
| NiCuNi + Epoxy | 20-28 μm | 48 hours | 72 hours |
| NiCuNi + Gold | 16-23 μm | 36 hours | 72 hours |
| NiCuNi + Silver | 16-23 μm | 24 hours | 48 hours |
| Zinc | 7-15 μm | 12 hours | 24 hours |
Each individual layer of Nickel and Copper are 5-7 μm thick. The Gold and Silver plating layers are 1-2 μm thick.
Test results shown to allow comparison between plating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.
Test results shown to allow comparison between plating options. Performance in your application under your specific test conditions may vary. Salt Spray testing conducted with a 5% NaCl solution, at 35°C. Pressure Cooker Test (PCT) conducted at 2 atm, 120°C at 100% RH.